宝钢40Cr模具钢_区别

宝钢40Cr模具钢_区别

　　40CR材料

　　40CR钢属于中等碳调节的钢。钢价中等且易于加工。经过适当的热处理后，可以获得韧性，塑料和磨损的耐药性。阳性火可以促进组织ballization并提高粗糙的加工性（硬度 <160HBW).The ignition of 550-570 ° C has the best comprehensive mechanical performance.The hardening of the steel is higher than 45 steel, which is suitable for high -frequency quenching, flame quenching and other surfaces and hardening treatment.

　　After the quality adjustment, it has good comprehensive force and incompleteness, good low temperature impact toughness and low gap sensitivity.The hard quenchtability of the steel is good, and it can be quenched to φ28 ~ φ60mm during water quenching, and it can be quenched to φ15 ~ φ40mm during oil quenching.In addition to the quality adjustment, the steel is also suitable for carbon nitrogen penetration and high -frequency induction quenching treatment.The processability is better. When the hardness is 174 to 229HBW, the relative processability is 60%.

　　40CR supply status

　　Antuction, hardness ≤207hbw.

　　40CR chemical composition

　　According to the standard GB/T3077-1999, the chemical composition of the steel (physical score): C0.37%～ 0.44%, Si0.17%～ 0.37%, MN0.50%～ 0.80%, CR0.80%～ 1.10%, Ni ≤ 0.30%.

　　40CR corresponding material

　　China GB standard number 40CR, German DIN standard material number 1.7035/1.7045, German DIN standard brand 41CR4/42CR4, British EN standard brand 18, British BS standard number 41CR4, French AFNOR standard brand 42C4, French NF standard number 38CR4/41CR4, Italy UNI Standard Dame Number 41CR4, Belgian NBN Standard Brand 42CR4, Swedish SS Standard Brand 2245, Spanish UNE Standard Brand 42CR4, Japan JIS Standard Script SCR440 (H)/SCR440, American ASIS/SAE/ASTM standard number 5140, ISO standard brand number 41CR4.

　　40CR physical performance

　　Critical point temperature (approximate value): ACCM = 780 ° C, AC1 = 780 ~ 770 ° C, AC3 = 840 ~ 805 ° C, ms = 335-328 ° C.

　　Wiring expansion coefficient: temperature 20 ~ 200 ℃/20 ～ 300 ℃/20 ~ 400 ℃/20-500 ℃/20-600 ℃

　　/20 ～ 700 ℃, line expansion coefficient (11.9 ~ 12.0) × 10-6k-1/(13.3 ~ 13.4) × 10-6k-1/(14.3 ~ 14.4) × 10-6k-1/(15.0 ～ 15.1) × 10-6k-1/(15.3 ～ 15.4) × 10-6k-1/(15.4 ~ 15.5) × 10-6k-1.

　　Thermal guidance rate: temperature 100 ℃/200 ℃/300 ℃/400 ℃/500 ℃/600 ℃, thermal conductivity 32.6 [w/(m · k)]/25.5 [w/m · k)].

　　40CR thermal processing specification

　　The heating temperature is 1150 ~ 1200 ° C, the start temperature starts at 1100 ~ 1150 ° C, the termination temperature is> 800°C和冷却方法：直径大于60mm时，缓慢冷。

　　40CR正常退火规格

　　退火温度为825?845°C，保存时间，炉子冷，硬度≤207hbw区别 。

　　40CR完全退火规格

　　退火温度为860?890°C，保存为2至3H，炉子冷后冷至500°C。

　　40CR阳性规格

　　正火的温度为850?870°C，热量是同一时间，空气冷，硬度≤250hbw。

　　40CR冷压粗糙软化处理规范

　　柔软度温度为740?760°C，保留热量为4至6H，然后以5-10°C/h至≤600°C的冷速度冷却。

　　治疗前的硬度≤217HBW，治疗后硬度≤163HBW。

　　40CR高温回收规范

　　恢复温度为680?700°C，冷却至≤600℃，空气冷却，硬度≤207hbw。治疗前的硬度≤217HBW，治疗后硬度≤163HBW。

　　40CR出生铁面粉保护规范规范

　　（670±10）℃×2H，用炉子加热，（710±10）°C×2H，用炉子冷却，（670±10）℃×2H，增加炉子的加热，（710±10 ）°C×2H，然后跟随关注者，跟随跟随者冷却炉子（670±10）°C×2H，用炉子加热，（710±10）°C×2H，总共三个循环，然后冷却至550°C，空气冷却，在处理后，硬度为153HBW。

　　40CR质量调整规范

　　淬火温度（850±10）°C，油冷却，点火温度（520±10）°C，水或油冷却。硬度≤250hbw。

　　40CR普通淬火和恢复规格

　　淬火温度为830?860°C，油冷，火为400?600°C，水或油在冷却。

　　40cr淬火+恢复+硼渗流过程

　　850°C淬火，在400°C下捕获，硬度40?45hrc; Boono盐浴配方（质量评分）：NACL15％+NA2B4O771％+SIC11％（SIC为140个网格粉末）；到850°C，恢复了400°C×40分钟，峰值的深度为0.06至0.08min，硬度为1200hv0.1。

　　40CR桩焊接维修过程

　　清洁污垢，保护二氧化碳气体的焊接，焊接线号H08MN2SIA，直径0.8mm，焊接电流100a的焊接电流，18-21V的电弧电压，使用短电路过渡，首先将零件均匀旋转至点燃电弧焊接，以便可以使用焊接道来制作焊接径。当通过螺旋向前推动时区别 ，焊接轨道均匀加热以防止轴变形。

　　控制零件在200°C下的表面温度，焊接后加热，并冷却。

　　40CR使用

　　可用于拉动霉菌和整形手术。

　　它可用于冷挤压打孔，重载的冷头，小打孔头和直径 <5-6mm in a thick steel plate in 10 to 25mm.

　　它可用于中型和小冲洗，小型服务寿命冷泵工具。

　　原铁碎屑的恢复规格可用于冷压形成模具。

　　粉末冶金压力。

　　在深层拳头Quench+恢复+硼渗漏处理后，平均使用寿命为10500，这增加了W18CR4V钢打孔的使用寿命的2至3倍。

　　使用40CR钢柱插头进行淬火+恢复+硼渗漏，而不是CR12MOV钢淬灭+恢复，使用寿命已从37,000增加到42,000件增加到44,000件。

　　40CR钢硼倾倒头代替W18CR4V高速钢服务寿命已从1,000件增加到2500件。

　　40CR钢锻造热淬火+实心硼稀土渗漏+淬火+低温恢复过程而不是5Crmnmo钢订单

　　活塞热锻造体支柱上的模具已从1500增加到2,000。

　　可用于预测杆。

　　它可用于制造具有较大尺寸，复杂形状和高精度的塑料模具。

　　可用于中型塑料模具。